中性快速固化硅酮密封胶，适用于一般密封及粘结如门窗、金属屋顶、排水沟、对玻璃、铝、不锈钢、砖、陶瓷及大部分金属及塑料均有极强粘结力。
主要性能特点:
1.单组分，易于操作
2.中性固化，无强烈的气味
3.快速固化
4.维持很好的柔韧性
5.与玻璃，大部分金属和塑料有极强粘结力
6.七种颜色可供选择：透明，白色，灰色，浅灰色，黑色，银色，棕色
包装：300ml硬支装，24支一箱

未固化的特性      
外观                                  膏状
邵氏硬度°A                     18                  ASTM C661
下垂度（W=20mm）         0                  JIS A1439
操作时间                        10分钟   
不粘手时间                     20分钟                JIS A1439
固化时间                         2天           8mm深@23℃，55%相对温度
已固化的特性   
外观                              弹性橡胶状      
挤用性                          ＞300ml/min     
最大抗拉强度              ＞1.2Mpa               ASTM D412
最大拉伸率                  350%                 ASTM D412
固化后使用温度        -53~149℃              ADCT-13A
弹性回复率                   ＞90%      
接口位移承受能力       ±25%                ASTM C719 
很适合用于出口，主要是因为污染指标测试

Brand: GE
Model: 168 neutral silicone sealant
  
Basic parameters
Uses: water, cracking, weathering
Size: 300ml hard sticks, a box of 24
Storage period: 12 months
 
Technical parameters
Elongation: 350%
Surface drying time (hours): 20 minutes
Melting point: 149 ℃
Freezing Point: -53 ℃
Tensile strength: 1.2 mPa
Neutral fast curing silicone sealant for general sealing and bonding, such as windows and doors, metal roof, gutters, glass, aluminum, stainless steel, bricks, ceramics and most metals and plastics are extremely strong bond strength.
Main features:
1. One-part, easy to operate
2. Neutral cure, no strong odor
3. Fast curing
4. To maintain good flexibility
5. And glass, most metals and plastics have strong adhesive force
6. Seven colors: transparent, white, gray, light gray, black, silver, brown
Packaging: 300ml hard sticks, a box of 24

Uncured properties
Appearance paste
Hardness ° A 18 ASTM C661
Ptosis degree (W = 20mm) 0 JIS A1439
Operating time 10 minutes
Sticky time of 20 minutes JIS A1439
Curing time of 2 days 8mm deep @ 23 ℃, 55% relative humidity
Characteristics have been cured
Elastic rubber-like appearance
Crowded with sexual> 300ml/min
The maximum tensile strength> 1.2Mpa ASTM D412
The maximum tensile rate of 350% ASTM D412
After curing temperature -53 ~ 149 ℃ ADCT-13A
Elastic recovery rate of> 90%
Interface displacement capacity of ± 25% ASTM C719
Very suitable for export, mainly because of pollution indicator test